BS EN 10089 56Si7 1.5026 Spring Steel Flat Bar
Sizes Range |
Thickness: 6-40 mm Width: 20-150 mm |
Chemical Composition |
C | Si | Mn | P max | S max |
0.52-0.60 | 1.6-2.0 | 0.6-0.9 | 0.025 | 0.025 |
HEAT TREATMENT:
FORGING:Hot forming temperature: 1050 – 850°C.
SOFT ANNEALING: Heat to 640 – 680°C, cool slowly in furnace. This will produce a maximum Brinell hardness of 248.
HARDENING: Harden from a temperature of 830 – 860°C followed by oil quenching.
TEMPERING:Tempering temperature: 430 – 500°C, air.
>>>Standard - EN 10089 Hot Rolled Steels for Quenched and Tempered Springs
| |
| >>>Steel Grades - GB: 60Si2MnA
- BS EN: 56Si7
- JIS: SUP7
|